A　kind　of　composite　material,　tungsten　wire-CVD　tungsten　was　fabricated　by　winding　tungsten　wire　on　the　substrate　periodically　in　the　CVD　process　using　the　homemade　CVD　device.　The　density,　composition　and　micro-hardness　were　tested　and　analyzed;　the　crushing　strength　was　calculated　according　to　crushing　test;　the　tensile　and　bending　curves　were　obtained　according　to　tensile　test　and　three-point　bending　test.　The　results　show　that　the　dense　coating　without　holes　can　be　obtained　when　the　chemical　reaction　temperature　is　controlled　at　550　degrees　C　and　the　flows　of　WF6　and　H-2　are　controlled　at　2　g/min　and　1　L/min,　respectively.　Compared　with　the　CVD　tungsten　samples　without　wound　tungsten　wire　under　the　same　process　conditions,　the　tungsten　wire-CVD　tungsten　composite　materials　still　possesses　high　purity　and　density,　the　similar　micro-hardness,　but　the　crushing　strength,　the　tensile　strength　and　the　bending　strength　are　improved　greatly.