The　epitaxial　La0.7Sr0.3MnO3/BaTiO3　bilayer　film　was　deposited　on　(0　0　1)　oriented　SrTiO3　single-crystal　substrate　by　pulsed　laser　deposition.　The　bilayer　film　possessed　inherent　ferromagnetic,　ferroelectric　properties.　The　frequency　dependence　of　magnetoelectric　(ME)　voltage　coefficient　revealed　a　strong　ME　coupling　from　0.1　kHz　to　100　kHz.　The　value　of　ME　voltage　coefficient　(alpha(E))　was　around　213　mV/cm　Oe　at　1　kHz,　which　was　at　least　one　order　of　magnitude　higher　than　other　reports　in　the　similar　structure　due　to　the　rather　low　dielectric　constant　of　BTO　film.　The　measured　value　of　alpha(E)　corresponded　to　the　theoretical　expectation　when　interface　coupling　coefficient　was　0.88.　(C)　2012　Elsevier　B.V.　All　rights　reserved.