A　composite　Au@Bi2Cu0.1V0.9O5.35　(BICUVOX10)　cathode　is　prepared　and　tested　as　a　ceramal　electrode　for　use　in　low-temperature　solid-oxide　fuel　cells　(SOFCs).　Au　powder　is　coated　onto　the　surface　of　BICUVOX10　from　an　aqueous　solution　of　the　chloride　with　NaBH4　as　a　reductant.　The　valence　of　the　surface　Au　is　identified　as　Au(0)　by　X-ray　photoelectron　spectroscopy　(XPS).　The　BICUVOX10　substrate　is　synthesized　from　V2O3,　CuO,　and　Bi2O3　and　then　investigated　by　field-emission　scanning　electron　microscopy　(SEM).　The　average　size　of　the　particles　is　estimated　to　be　100　nm　after　milling　with　a　planetary　ball-mill.　The　core-shell　structure　of　Au@BICUVOX10　is　confirmed　by　transmission　electron　microscopy　(TEM).　The　two-dimensional　coefficient　of　thermal　expansion　(CTE)　and　the　conductivities　of　mixed　powders　with　different　proportions　of　Au　is　also　tested　from　room　temperature　to　600　degrees　C.　A　single　fuel　cell　is　fabricated　with　Au@BICUVOX10　as　the　cathode,　NiO/GDC　(Gd0.1Ce0.9O1.95)　as　the　supporting　anode,　and　GDC　as　the　electrolyte.　The　electrochemical　performance　is　tested　and　the　highest　power　densities　of　the　fuel　cell　are　determined　to　be　127,　206,　359,　469,　and　474　mW　cm(-2)　at　450,　500,　525,　550,　and　575　degrees　C,　respectively.　Finally,　the　stability　of　the　single　SOFC　is　tested,　whereupon　it　is　found　that　its　output　is　maintained　for　at　least　the　first　20　h.　(C)　2009　Elsevier　B.V.　All　rights　reserved.