Bulk　nanocrystalline　gadolinium　metal　was　prepared　using　spark　plasma　sintering　(SPS)　and　subsequent　annealing　process.　The　SPS　Gd　metal　had　a　single　phase　with　a　mean　grain　size　of　about　10　nm.　A　pressure-induced　C-axis　crystal　texture　was　found　in　the　SPS　Gd　sample.　With　the　decrease　of　Gd　grains　from　micrometer　to　nanometer　range,　the　Curie　temperature　T-C　decreased　by　10.7　K　and　the　magnetic　moment　per　Gd　atom　at　5　K　dropped　noticeably　from　7.81　mu(B)　to　6.31　mu(B).　These　results　indicate　the　remarkable　influence　of　the　nanostructure　on　the　magnetism　of　Gd　due　to　the　finite　size　effect.　(c)　2006　American　Institute　of　Physics.