The　behaviour　under　cyclic　bending　and　in　particular　the　fatigue　properties　of　shape　memory　alloy　(SMA)　bars　are　important　for　civil　engineering　applications.　In　this　paper,　structural　and　functional　fatigue　is　studied　for　both　NiTi-　and　copper-based　shape　memory　alloys.　The　results　are　presented　from　cyclic　bending　tests　on　7　mm　diameter　NiTi　and　12　mm　diameter　CuAlMn　SMA　bars　targeted　at　100,000　cycles.　During　the　tests,　dynamic　loading　at　1　Hz,　5　Hz,　and　8　Hz　was　applied　for　different　strain　levels　(0.5%,　1%,　2%,　and　6%).　The　stress-strain　curve,　damping　ratio,　and　secant　stiffness　were　analysed　for　material　characterisation,　and　the　evolution　of　these　parameters　was　studied　to　assess　functional　fatigue.　The　fatigue　life　is　extended　dramatically　when　the　strain　is　below　1%,　and　the　structural　fatigue　life　of　CuAlMn　is　shown　to　be　better　than　that　of　NiTi　and　to　depend　on　the　loading　rate.　However,　decay　in　stiffness　can　be　found　in　the　CuAlMn　SMA,　which　is　considered　to　be　caused　particularly　by　its　long　grain　boundary.