Biocorrosion　or　microbiologically　influenced　corrosion　(MIC)　is　a　major　problem　in　many　industries,　especially　the　oil　and　gas　industry.　Biofilms　are　the　culprits　of　MIC.　In　this　work,　D-amino　acids　were　used　to　enhance　two　biocides,　namely　alkyldimethylbenzylammonium　chloride　(ADBAC)　and　tributyl　tetradecyl　phosphonium　chloride　(TTPC),　to　treat　a　tough　and　corrosive　field　biofilm　consortium　on　C1018　carbon　steel　coupons.　An　equi-mass　D-amino　acid　mixture　(＇D-mix＇)　of　four　D-amino　acids　(D-methionine,　D-tyrosine,　D-leucine,　and　D-tryptophan)　at　a　total　concentration　of　50　ppm　(w/w)　was　tested.　The　cocktails　of　60　ppm　ADBAC　+　50　ppm　D-mix　and　40　ppm　TTPC　+　50　ppm　D-mix　both　achieved　a　3-log　reduction　of　the　sessile　cell　count　of　sulfate　reducing　bacteria　(SRB)　in　the　7-day　biofilm　prevention　test　compared　with　a　1-log　reduction　achieved　by　60　ppm　ADBAC　and　40　ppm　TTPC　alone　separately.　In　the　3-hour　biofilm　removal　test　that　started　with　mature　biofilms　on　C1018　carbon　steel　coupon　surfaces,　the　cocktails　of　150　ppm　ADBAC　+　50　ppm　D-mix　and　100　ppm　TTPC　+　50　ppm　D-mix　both　achieved　a　2-log　reduction　compared　with　a　1-log　reduction　achieved　by　150　ppm　ADBAC　and　100　ppm　TTPC　alone　separately.　In　all　the　tests,　D-mix　alone　showed　no　log　reduction.　Scanning　electron　microscope　images　and　confocal　laser　scanning　microscope　images　supported　the　results.　©　2016　by　NACE　International.