NaCl1-xBrxO3　single　crystals　were　prepared　by　unidirectional　crystallization.　The　influences　of　the　composition　on　structure.　quality,　and　optical　properties　of　NaCl1-xBrxO3　crystals　were　investigated.　X-ray　powder　diffraction　analysis　revealed　that　the　diffraction　patterns　for　the　NaCl1-xBrxO3　crystals　have　almost　the　same　set　of　peaks　as　those　of　NaClO3　and　NaBrO3,　except　that　an　extra　very　weak　forbidden　(100)　diffraction　peak　was　detected　at　about　13.3　degrees　2　theta　for　crystals　grown　from　solutions　of　BrO3-　similar　to　15-70　at.　%　(i.e.,　x=0.15-0.70).　These　crystals　can,　therefore,　be　considered　to　have　a　distorted　cubic　structure　closely　related　to　the　cubic　structures　of　NaClO3　(x=0)　and　NaBrO3　(x=1).　Our　study　also　found　that　good-quality　crystals　can　only　be　obtained　in　two　doping　ranges　(x　＞　0.75　or　x　＜　0.10).　Outside　these　two　ranges,　the　crystals　tended　to　crack　and　even　became　opaque.　Lattice　distortions　in　the　crystals　were　the　probable　cause　as　revealed　by　X-ray　powder　diffraction　patterns.　The　optical　activity　of　NaCl1-xBrxO3　crystals　measured　by　a　laser　was　found　to　decrease　from　2.89　to　2.01　degrees/mm　with　increasing　value　of　x　from　0　to　0.02.　Stimulated　Raman　scattering　of　NaBr0.90Cl0.10O3　Crystals　was　measured　using　a　0.532-mu　m　ps　laser　as　a　pump　source　and　four　anti-Stokes　lines　plus　six　Stokes　lines　were　observed.　The　fourth　anti-Stokes　emission　was　found　to　be　at　454.5　nm　and　the　sixth　Stokes　emission　at　713.6　nm.　Its　Raman　gain　coefficient　was　determined　to　be　18.4　cm/Gw.　(C)　2009　International　Centre　for　Diffraction　Data.　[DOI:　10.1154/1.3193561]