Developing　novel　oxygen　evolution　reaction　(OER)　and　hydrogen　evolution　reaction　(HER)　catalysts　is　vital　for　water　splitting.　Here,　carbon　black　(CB)　and　nickel　carbonyl　powder　(NCP)　are　used　as　components,　and　the　nonionic　surfactant　polyvinyl　pyrrolidone　(PVP)　is　used　as　a　shape-controlled　capping　agent　to　easily　prepare　layered　double　(Ni,　Fe)　hydroxide　(NiFe-LDH)　electrodes.　Scanning　electron　microscopy　observation　and　X-ray　photoelectron　spectra　analysis　show　that　the　Fe2+　-doped　layered　double　hydroxide　is　grown　in　situ　on　nickel　foam　(NF).　CB　(XC-72)　and　NCP　further　improve　the　electrical　conductivity.　At　10　mA.cm(-2),　the　overpotentials　of　the　OER　and　HER　are　203　mV　and　83　mV,　respectively,　in　1　M　KOH.　Only　1.48　V　is　needed　when　both　electrodes　are　applied　for　water　splitting,　and　it　has　a　stability　of　more　than　100　h.　This　work　can　be　used　as　a　medium　to　elevate　the　OER　and　HER　performance　of　NiFe-LDH-based　catalysts.　(C)　2021　Hydrogen　Energy　Publications　LLC.　Published　by　Elsevier　Ltd.　All　rights　reserved.