The　crystal　structure,　martensitic　transformation　and　magnetocaloric　effect　have　been　studied　in　all-d-metal　Ni35Co15Mn33Fe2Ti15　alloy　ribbons　with　different　wheel　speeds　(15　m/s　(S15),　30　m/s　(S30),　and　45　m/s　(S45)).　All　three　ribbons　crystalize　in　B2-ordered　structure　at　room　temperature　with　crystal　constants　of　5.893(2)　angstrom,　5.898(4)　angstrom,　and　5.898(6)　angstrom,　respectively.　With　the　increase　of　wheel　speed,　the　martensitic　transformation　temperature　decreases　from　230　K　to　210　K,　the　Curie　temperature　increases　slightly　from　371　K　to　378　K.　At　the　same　time,　magnetic　entropy　change　(Delta　S-m)　is　also　enhanced,　as　well　as　refrigeration　capacity　(RC).　The　maximum　Delta　S-m　of　15.6(39.7)　J/kg　center　dot　K　and　RC　of　85.5　(212.7)　J/kg　under　Delta　H　=　20　(50)　kOe　(1　Oe　=　79.5775　A　center　dot　m(-1))　appear　in　S45.　The　results　indicate　that　the　ribbons　could　be　the　candidate　for　solid-state　magnetic　refrigeration　materials.