PbS　quantum　dots　(QDs)　are　appropriate　for　use　in　tunable　optoelectronic　devices　such　as　optical　amplifiers　because　of　their　large　Bohr　exciton　radii　(18　nm).　Laser-assisted　local　heating　around　Ag　NPs　can　provide　an　effective　method　for　site　selective　precipitation　and　for　controlling　the　size　of　QDs.　Continuous　wave　(CW)　laser　irradiation　has　been　applied　on　a　Ag+-ion　exchanged　glass　which　lead　to　the　precipitation　of　QDs　PbS　QDs　of　5-nm　diameter　were　precipitated　after　3　min　of　CW　laser　illumination　at　1.5　W.　The　PbS　QDs　showed　a　PL　peak　at　λ　∼　1490　nm,　which　shifted　toward　longer　wavelength　side　as　duration　of　Ag+　ion　exchange　and　of　laser　illumination　increased.　This　method　was　further　applied　to　prepare　a　rod　containing　three　sections　with　different　diameters　of　PbS　QDs　to　propose　the　possibility　of　developing　broadband　amplifiers　to　cover　the　1.3–1.7　μm　communication　window　using　one　glass　fiber.　Co2+　also　absorbs　532　nm　laser　light　and　converts　it　to　thermal　energy　that　results　in　the　precipitation　of　PbS　QDs　in　the　glass　matrix.　The　emission　peak　of　the　QDs　covers　1020　nm　＜　λ　＜　1245　nm　as　laser　power　was　increased　from　6　to　7　W/cm2.　Temperature　in　the　glass　increased　to　∼518　°C　when　it　was　illuminated　at　the　intensity　of　6　W/cm2.　©　2022　The　Authors