A　cheap　PMMA　was　chosen　as　the　substrate　instead　of　expensive　silicon　or　glass,　and　a　248　nm　excimer　laser　with　flexible　and　auto　character　replaced　complex　lithography　as　a　new　fabrication　technique.　A　PMMA　(48　mm　x　67　mm　x　1　mm)　based　micro　flow　through　PCR　chip　with　20　cycles　was　fabricated　at　19　kV　and　18　mm/min　excimer　laser　parameters.　The　section　of　the　microchannel　was　trapezoid,　and　its　bottom　surface　roughness　was　less　than　0.5　mu　m.　The　microchannel　had　a　width　of　104　mu　m,　a　depth　of　56　mu　m,　and　a　length　of　2　060　mm.　It　cost　about　110　min　to　finish　the　total　length.　Then　the　chip　was　bonded　together　with　another　cover　chip　at　105　degrees　C,　160　N　and　20　min　parameters.　It　could　endure　0.85　MPa　pressure　and　seal　micro　fluid　well　after　sample　injection　experiment.　In　the　end,　the　chip　was　integrated　via　the　temperature　control　system.　Three　micro　PID　temperature　controllers　were　chosen　to　control　the　temperature　and　gained　+/-　0.2　degrees　C　temperature　control　precision.　The　temperature　grads　between　the　three　temperature　zones　were　16.5　and　22.2　degrees　C,　respectively.　Finally　170　by　DNA　fragments　was　amplified　by　using　this　chip.