In　this　paper,　high　quality　cutting　of　1　mm　dense　Al2O3　electronic　ceramic　processed　by　a　fiber　laser　with　spot　diameter　of　15　pm　was　reported.　The　narrow　kerf　with　30　mu　m　width　was　obtained　with　laser　power　of　100　W.　300　W　is　the　laser　power　threshold　of　the　kerf　enlargement.　Under　higher　laser　power,　the　ceramics　can　be　damage-free　cut　with　higher　cutting　speed.　Striation-free　cutting　could　be　achieved　at　1000　W　laser　power　with　a　cutting　speed　of　350　mm/s.　The　ratio　of　cutting　speed　to　laser　power　for　striation-free　cutting　was　determined　as　0.35.　The　black　cutting　surface　was　due　to　the　mass　tetragonal　alumina　induced　by　N-2　as　assist　gas.