Abstract：
The aging behavior and the strengthening mechanism of the Si microalloyed Al-Zn-Mg-Cu alloy was investigated by means of microhardness tests, tensile properties tests and transmission electron microscope. It was found that the addition of Si element enhanced the microhardness and strength of Al-Zn-Mg-Cu alloy after aging at 125 degrees C, 175 degrees C and 225 degrees C. The age hardening effect of Al-Zn-Mg-Cu alloy gradually deteriorates with the increase of aging temperature, while the age hardening effect of Si-containing Al-Zn-Mg-Cu alloy at different aging temperature are stable. TEM results shows that the intragranular microstructure of the Si microalloyed alloy contained a fine dispersed, lath-like precipitate. This lath-like precipitation phase significantly improves the strength of the alloy and exhibit thermal stability, it is considered to be the GPB-II zone.
Keyword：
Reprint Author's Address：
Email：
Source ：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN： 0921-5093
Year： 2022
Volume： 852
6 . 4
JCR@2022
6 . 4 0 0
JCR@2022
ESI Discipline： MATERIALS SCIENCE;
ESI HC Threshold：66
JCR Journal Grade：1
CAS Journal Grade：1
Cited Count：
SCOPUS Cited Count：
ESI Highly Cited Papers on the List： 0 Unfold All
WanFang Cited Count：
Chinese Cited Count：
30 Days PV： 0
Affiliated Colleges：