Alumina　ceramics　with　different　unit　numbers　and　gradient　modes　were　prepared　by　digital　light　processing　(DLP)　3D　printing　technology.　The　side　length　of　each　functional　gradient　structure　was　10　mm,　the　porosity　ratio　was　controlled　to　70%,　and　the　number　of　units　were　(1　x　1　x　1　unit)　and　(2　x　2　x　2　unit)　respectively.　The　different　gradient　modes　were　named　FCC,　GFCC-1,　GFCC-2　and　GFCC-3.　SEM,　XRD,　and　other　characterization　methods　proved　that　these　gradient　structures　of　alumina　ceramics　had　only　alpha-Al2O3　phase　and　good　surface　morphology.　The　mechanical　properties　and　energy　absorption　properties　of　alumina　ceramics　with　different　functional　gradient　structures　were　studied　by　compression　test.　The　results　show　that　the　gradient　structure　with　1　x　1　x　1　unit　has　better　mechanical　properties　and　energy　absorption　properties　when　the　number　of　units　is　different.　When　the　number　of　units　is　the　same,　GFCC-2　and　GFCC-3　gradient　structures　have　better　compressive　performance　and　energy　absorption　potential　than　FCC　structures.　The　GFCC-2　gradient　structure　with　1　x　1　x　1　unit　has　a　maximum　compressive　strength　of　19.62　MPa　and　a　maximum　energy　absorption　value　of　2.72　x　105　J/m3.　The　good　performance　of　such　functional　gradient　structures　can　provide　new　ideas　for　the　design　of　lightweight　and　compressive　energy　absorption　structures　in　the　future.