Ultra-fast　growth　(up　to　100　nm　s−1)　of　high　temperature　superconducting　film　was　demonstrated　by　using　an　advanced　pulsed　laser　deposition　technique.　Highly　textured　EuBa2Cu3O7−δ　　　　　　　　　　　　　　　　(EuBCO)　film　with　8　mol.%　of　BaHfO3　(BHO)　was　deposited　on　the　IBAD-based　Hastelloy　substrates.　Structure　characterizations　reveal　formation　of　high　density　of　BHO　nanocolumns　with　diameter　of　∼5　nm　in　the　film,　which　is　well　beyond　the　expectation.　Comparison　study　on　different　amount　of　BHO　in　EBCO　film　confirmed　that　nanocolumn　formation　strongly　depends　on　the　dopant　level.　The　epitaxial　growth　process　of　BHO　is　dominated　by　ultra-fast　self-assembly　associated　with　enhanced　diffusion　of　high　flux　element　and　liquid　phase.　Due　to　the　correlated　pinning　landscape,　a　pronounced　broad　peak　appears　at　B//c　in　the　J　　　　　　　　　　　　　　　c(θ)　curves　at　30　K　5　T,　while　a　strong　pinning　force　of　about　900　GN　m−3　at　4.2　K,　10　T　(B//c)　are　achieved.