The　goal　of　current　research　is　to　focus　on　exploring　the　effects　of　various　MgO/SiO2　2　ratios,　emphasizing　their　impact　on　the　structure　properties　and　advancing　the　catalytic　activity　and　the　chemical　life　span　of　Ni-catalysts　by　an　exciting　mixture　of　SiO2　2　and　MgO　to　generate　COx-bare　hydrogen　and　nanocarbon　simultaneously　from　methane　decomposition　reactions.　SiO2/MgO　2　/MgO　mixed　oxides　with　different　ratios　(0.5,　1,　and　2)　were　ready　via　a　facile　co-precipitation　method　from　magnesium　nitrate　and　sodium　metasilicate　and　used　as　supports　for　various　nickel　contents　(30,　40,　50,　and　60　wt%)　followed　by　an　impregnation　technique.　Different　analytical　techniques,　such　as　XRD,　BET,　SEM,　EDS,　H2-TPR,　2-TPR,　and　TPO,　were　used　to　characterize　the　catalysts　before　and　after　the　catalytic　runs.　The　prepared　catalysts　with　various　SiO2/MgO　2　/MgO　molar　ratios　depicted　the　BET　surface　area　limiting　from　37.9　to　143.4　m　2　g-　1　,　indicating　remarkable　surface　improvements.　The　vast　CH4　4　conversion　of　64　%　earned　on　the　50　wt%　Ni/SiO2　&　sdot;MgO　2　&　sdot;　MgO　at　575　degrees　C.　Moreover,　lower　deactivation　was　detected　regarding　this　catalyst　at　600　min　on　stream.